Título: | Report of the key comparison CCQM-K88 : determination of lead in lead-free solder containing silver and copper |
Fuente: | Metrología, 50 |
Autor/es: | Hioki, Akiharu; Nonose, Naoko; Liandi, Ma; Jingbo, Chao; Liuxing, Feng; Chao, Wei; Cho, Kyung Haeng; Suh, Jung Ki; Min, Hyung Sik; Lim, Youngran; Recknagel, Sebastian; Koenig, Maren; Vogl, Jochen; Caciano de Sena, Rodrigo; dos Reis, Lindomar Augusto; Borinsky, Mónica; Puelles, Mabel; Hatamleh, Nadia; Acosta, Osvaldo; Turk, Gregory; Rabb, Savelas; Sturgeon, Ralph; Methven, Brad; Rienitz, Olaf; Jaehrling, Reinhard; Konopelko, L. A.; Kustikov, Yu. A.; Kozyreva, S. B.; Korzh, A. A. |
Materias: | Metrología; Plomo; Soldadura; Cobre; Plata; Determinación (química); Instrumentos de medición; Espectroscopía; Incertidumbre; Mediciones |
Editor/Edición: | IOP Publishing; 2013 |
Licencia: | https://creativecommons.org/licenses/by/3.0/ |
Afiliaciones: | Hioki, Akiharu. National Metrology Institute of Japan (NMIJ); Japón Nonose, Naoko. National Metrology Institute of Japan (NMIJ); Japón Liandi, Ma. National Institute of Metrology (NIM); China Jingbo, Chao. National Institute of Metrology (NIM); China Liuxing, Feng. National Institute of Metrology (NIM); China Chao, Wei. National Institute of Metrology (NIM); China Cho, Kyung Haeng. Korea Research Institute of Standards and Science (KRISS); Corea del Sur Suh, Jung Ki. Korea Research Institute of Standards and Science (KRISS); Corea del Sur Min, Hyung Sik. Korea Research Institute of Standards and Science (KRISS); Corea del Sur Lim, Youngran. Korea Research Institute of Standards and Science (KRISS); Corea del Sur Recknagel, Sebastian. Federal Institute for Materials Research and Testing (BAM); Alemania Koenig, Maren. Federal Institute for Materials Research and Testing (BAM); Alemania Vogl, Jochen. Federal Institute for Materials Research and Testing (BAM); Alemania Caciano de Sena, Rodrigo. Instituto Nacional de Metrologia, Qualidade e Tecnologia (INMetro); Brasil dos Reis, Lindomar Augusto. Instituto Nacional de Metrologia, Qualidade e Tecnologia (INMetro); Brasil Borinsky, Mónica. Instituto Nacional de Tecnología Industrial (INTI); Argentina Puelles, Mabel. Instituto Nacional de Tecnología Industrial (INTI); Argentina Hatamleh, Nadia. Instituto Nacional de Tecnología Industrial (INTI); Argentina Acosta, Osvaldo. Instituto Nacional de Tecnología Industrial (INTI); Argentina Turk, Gregory. National Institute of Standards and Technology (NIST); Estados Unidos Rabb, Savelas. National Institute of Standards and Technology (NIST); Estados Unidos Sturgeon, Ralph. National Research Council (NRC); Canadá Methven, Brad. National Research Council (NRC); Canadá Rienitz, Olaf. Physikalisch-Technische Bundesanstalt (PTB); Alemania Jaehrling, Reinhard. Physikalisch-Technische Bundesanstalt (PTB); Alemania Konopelko, L. A. D. I. Mendeleev Institute for Metrology (VNIIM); Rusia Kustikov, Yu. A. D. I. Mendeleev Institute for Metrology (VNIIM); Rusia Kozyreva, S. B. D. I. Mendeleev Institute for Metrology (VNIIM); Rusia Korzh, A. A. D. I. Mendeleev Institute for Metrology (VNIIM); Rusia |
|
|
Resumen: | The CCQM-K88 key comparison was organised by the Inorganic Analysis Working Group of CCQM to test the abilities of the national metrology institutes to measure the mass fraction of lead in lead-free solder containing silver and copper. National Metrology Institute of Japan (NMIJ), National Institute of Metrology P. R. China (NIM) and Korea Research Institute of Standards and Science (KRISS) acted as the coordinating laboratories. The participants used different measurement methods, though most of them used inductively coupled plasma optical emission spectrometry (ICP-OES) or isotope-dilution inductively coupled plasma mass spectrometry (ID-ICP-MS). Accounting for relative expanded uncertainty, comparability of measurement results was successfully demonstrated by the participating NMIs for the measurement of the mass fraction of lead in lead-free solder at the level of 200 mg/kg. It is expected that metals at mass fractions greater than approximately100 mg/kg in lead-free solder containing silver and copper can be determined by each participant using the same technique(s) employed for this key comparison to achieve similar uncertainties mentioned in the present report. |
Descargar |
Ver+/-
Report of the key comparison CCQM-K88 Determination of lead in lead-free solder containing silver and copper (Final Report) Authors: Akiharu Hioki and Naoko Nonose (NMIJ),*1 Ma Liandi, Chao Jingbo, Feng Liuxing and Wei Chao (NIM),*2 Kyung Haeng Cho, Jung Ki Suh, Hyung Sik Min and Youngran Lim (KRISS),*3 Sebastian Recknagel, Maren Koenig and Jochen Vogl (BAM),*4 Rodrigo Caciano de Sena and Lindomar Augusto dos Reis (INMETRO),*5 Mónica Borinsky, Mabel Puelles, Nadia Hatamleh and Osvaldo Acosta (INTI),*6 Gregory Turk and Savelas Rabb (NIST),*7 Ralph Sturgeon and Brad Methven (NRCC),*8 Olaf Rienitz and Reinhard Jaehrling (PTB),*9 L. A. Konopelko, Yu.A. Kustikov, S. B. Kozyreva and A. A. Korzh (VNIIM).*10 *1 National Metrology Institute of Japan *2 National Institute of Metrology P. R. China *3 Korea Research Institute of Standards and Science *4 Federal Institute for Materials Research and Testing *5 National Institute of Metrology, Standardization and Industrial Quality *6 National Institute of Industrial Technology *7 National Institute of Standards and Technology *8 National Research Council Canada *9 Federal Institute of Physical and Technical Affairs *10 All-Russia D. I. Mendeleev Scientific and Research Institute for Metrology Coordinated by: Akiharu Hioki (NMIJ), Ma Liandi (NIM), Kyung-Haeng Cho (KRISS) Abstract The CCQM-K88 key comparison was organised by the Inorganic Analysis Working Group of CCQM to test the abilities of the national metrology institutes to measure the mass fraction of lead in lead-free solder containing silver and copper. National Metrology Institute of Japan (NMIJ), National Institute of Metrology P. R. China (NIM) and Korea Research Institute of Standards and Science (KRISS) acted as the coordinating laboratories. The participants used different measurement methods, though most of them used inductively coupled plasma optical emission spectrometry (ICP-OES) or isotope-dilution inductively coupled plasma mass spectrometry (ID-ICP-MS). Accounting for relative expanded uncertainty, comparability of measurement results was successfully demonstrated by the participating NMIs for the measurement of the mass fraction of lead in lead-free solder at the level of 200 mg/kg. It is expected that metals at mass fractions greater than approximately100 mg/kg in lead-free solder containing silver and copper can be determined by each participant using the same technique(s) employed for this key comparison to achieve similar uncertainties mentioned in the present report. 1 1 Introduction Solder is a ubiquitous industrial material and recent interest in lead-free solders has arisen from the viewpoint of the RoHS directive. Therefore, accurate measurements of lead in lead-free solders, especially containing silver and copper, are important. To date, only low alloy steel (P25 and K33+P56) and a copper alloy (P76 and K64) have been used as materials for CCQM comparisons in the field of metals and metal alloys. Since the main constituent of solders is usually tin, the pilot study CCQM-P119 extended the field of comparisons to another important type of metals and metal alloys. Following the pilot study CCQM-P119, National Metrology Institute of Japan (NMIJ), National Institute of Metrology P. R. China (NIM) and Korea Research Institute of Standards and Science (KRISS) proposed a key comparison of "Determination of lead in lead-free solder containing silver and copper” at the Inorganic Analysis Working Group (IAWG) meeting held April 13-14, 2010. At the CCQM meeting following the IAWG meeting, the proposal was agreed as CCQMK88 and NMIJ, NIM and KRISS were designated as coordinating laboratories. The element in this comparison was lead in the solder matrix at a mass-fraction between 100 mg/kg and 600 mg/kg. Each participant could use any suitable method(s) of measurement. Four measurements of the element had to be carried out by each participant. The homogeneity of the material used in this study had been investigated prior to the comparison. This is the first CCQM key comparison in the field of tin-based alloy analysis. The comparison results were discussed at the IAWG meetings held April 11-12, 2011, November 1-2, 2011 and April 16-17, 2012. It was decided that a parallel pilot study designated CCQM-P125 would be conducted, in which the same samples measured by the CCQM-K88 participants would also be used. 2 2 List of Participants Table 1 contains the full names of all participating NMIs. In the context of the current concept of the CIPM-MRA, different CMCs which refer to the same key comparison should be acceptable. Therefore, there is no problem with both BAM and PTB participating in this key comparison provided they do not both have CMCs for the same measurements. Table 1 List of participating NMIs No. 1 2 3 4 5 6 7 8 9 10 Participant BAM Federal Institute for Materials Research and Testing INMETRO National Institute of Metrology, Standardization and Industrial Quality INTI National Institute of Industrial Technology KRISS Korea Research Institute of Standards and Science NIM National Institute of Metrology P. R. China NIST National Institute of Standards and Technology NMIJ National Metrology Institute of Japan NRC National Research Council Canada PTB Federal Institute of Physical and Technical Affairs VNIIM All-Russia D. I. Mendeleev Scientific and Research Institute for Metrology Country Germany Brazil Argentina Rep. of Korea P. R. China USA Japan Canada Germany Russia 3 Samples The comparison material is a lead-free solder (Sn 96.5 %, Ag 3 % and Cu 0.5 %) containing between 100 mg/kg and 600 mg/kg of lead. The measurand to be determined is the mass fraction of lead. The material consists of short pieces (less than 0.1 g each) made by cutting long wires. Each participant received approximately 10 g of the lead-free solder and were instructed to keep the material at ambient laboratory temperature after receipt. No special treatment of the sample, such as drying, was required before use; however, it was noted that it should be kept in a silica-gel desiccator before weighing. The homogeneity of the material, expressed as the relative standard deviation (RSD) of the mass fraction of lead, was 0.13 % (RSD) according to results for determination of lead by isotopedilution inductively coupled plasma mass spectrometry (ID-ICP-MS or IDMS) using a sample size of about 0.2 g. Though the homogeneity indicated in the technical protocol was 0.8 % (RSD) based on analysis by inductively coupled plasma optical emission spectrometry (ICP-OES or OES), it was substantially better according to the more precise ID-ICP-MS measurements. Based on the sample size for the homogeneity test, the use of more than 0.2 g sample for each measurement was strongly recommended. The homogeneity value was expressed for a single sub-sampling of 0.2 g; it should be divided by the square root of 4 for the homogeneity corresponding to the average arising from four sub-samplings. 3 The samples were distributed to the participants from NMIJ by EMS mail in July, 2010, except for BAM, PTB and KEBS (in August, 2010). Finally, all samples reached their destinations safely. The contact persons are given in Table 2. Table 2 List of contact persons of the participants Participant BAM Contact person Sebastian Recknagel INMETRO Rodrigo Caciano de Sena INTI KRISS NIM NIST NMIJ NRC PTB VNIIM Mónica Borinsky Kyung Haeng Cho Ma Liandi Gregory Turk Akiharu Hioki Ralph Sturgeon Olaf Rienitz L.A. Konopelko 4 Technical Protocol The technical protocol, attached as Annex A, instructed participants concerning treatment of the samples, methods of measurement, reporting of results and the time schedule. The deadline for the reporting of results was originally intended to be September 20, 2010 in the protocol; it was, however, postponed to December 31, 2010. 5 Methods of Measurement Participants were allowed to use any suitable method(s) of measurement. Though most of the results were obtained by ICP-OES or ID-ICP-MS, isotope-dilution thermal ionization mass spectrometry (ID-TIMS) and glow dishcarge mass spectrometry (GDMS) were also employed by one participant each. The number of results by each method is summarized in Table 3. Table 3 Number of results by each method for CCQM-K88 Method ICP-OES ID-ICP-MS ID-TIMS GDMS Number of results reported 4 4 1 1 Total number 10 4 6 Results Results, given in Table 4, include information on the measurement methods; results are illustrated graphically in Figure 1. The half of the bar of each data in the Figure 1 indicates the reported combined standard uncertainty (k = 1). The Figure contains a solid, horizontal line representing the median of the IDMS or ID-TIMS data. The uncertainty of the median was based on the estimate according to median(|xi-median|)/0.6745, where xi is each reported value. The dashed, horizontal lines indicate the range of the combined standard uncertainty (k = 1) of the median. The median for the IDMS or ID-TIMS data and its expanded uncertainty (k = 2) are 197.2 mg/kg and 0.93 mg/kg; the expanded uncertainty 0.9 mg/kg was used for calculating the uncertainty of the degree of equivalence (vide infra). The arithmetic mean of the IDMS or IDTIMS data for the measurand is also represented in Figure 1. The half of the bar of the arithmetic mean indicates the combined standard uncertainty (k = 1) based on the standard deviation of the mean. The reference value (RV) is discussed in the following section 5 Table 4 Results for lead of CCQM-K88 Participant Measurement Method INMETRO ICP-OES VNIIM ICP-OES, with external calibration Decomposition Method HCl:H2O2 (3:2); microwave digestion; no Pb detected in precipitation HNO3:HF (5:1) digestion Materials used for calibration Pb standard solution (NIST SRM 3128) Reported value / mass fraction (mg/kg) 179 Combined standard uncertainty / mass fraction (mg/kg) (k=1) 2 CRM of Pb 194.2 5 solution (GSO 7447-98) NIM ID-ICP-MS H2O2/HF digestion NIM primary 195.8 1.3 (207/208, Q-ICP- assay standard MS) of Pb NMIJ ID-ICP-MS HNO3/HF digestion NMIJ primary 196.7 0.76 standard solution KRISS ID-ICP-MS (Q- HNO3/HCl digestion KRISS primary 197.2 1.0 ICP-MS) assay standard of Pb PTB ID-ICP-MS (HR- HCl/HNO3 digestion calibration 197.9 0.95 ICP-MS) standard (BAM-A- primary-Pb-1) BAM ID-TIMS HNO3 digestion by primary 198.29 0.25 high pressure asher reference material BAMY004 INTI ICP-OES, HNO3/HF 5+1 Pb standard 199 2 calibration/matrix digestion solution (NIST matching SRM 3128) NIST ICP-OES, HNO3/HF digestion NIST SRM 199.43 0.35 standard addition 3128 standard calibration solution (CRM for Pb) NRC GDMS Direct calibrated 202.4 9.3 measurement against lead- free solder CRM with similar composition (NMIJ CRM 8203-a) 6 mass fraction of Pb (mg/kg) 210 Pb 200 190 (mean) (median) ± 1 % 180 170 OES IDMS IDMS ID- OES GDMS OES IDMS IDMS TIMS OES INMETROVNIIM NIM NMIJKRISS PTB BAM INTI NIST NRC Fig. 1 Results for Pb of CCQM-K88 aritmhmedeiatinc mean The half of each bar indicates the combined standard uncertainty (k =1). 7 Discussion No clearly observed differences among the measurement methods (including the acids used for digestion) employed are evident from the results. Most of the reported data are within ±2 % relative to the median, except for a limited number of results. In order to easily compare the results with each other, the reference value (RV) was estimated and an equivalence statement was made. At the IAWG meeting held April 11-12, 2011, it was decided that the RV should be estimated from the IDMS data, including the ID-TIMS value. For reference, some candidates for the RV are shown in Table 5; n=10 indicates that all submitted results were used for calculating the estimate. The variance due to heterogeneity was not included in the calculation of each expanded uncertainty. From the viewpoint of simplicity and robustness, the median is recommended as the RV for this comparison. If the homogeneity corresponding to the average from four sub-samplings is included, the expanded uncertainty of the median, for example, becomes 0.96 mg/kg. 7 Table 5. Candidates for an RV of lead for CCQM-K88 Mean (only IDMS & ID-TIMS) Mean (n=10) Median (only IDMS & ID-TIMS) Median (n=10) MMmedian (only IDMS & ID-TIMS) MMmedian (n=10) Weighted mean (usual weight) (n=10) Weighted mean (mild weight) (n=10) Value / Expanded uncertainty mass fraction (k=2) / (mg/kg) mass fraction (mg/kg) *1 197.2 0.9 *1 196.0 4.0 *2 197.2 0.9 *2 197.6 1.5 *3 197.3 0.9 *3 197.5 1.5 198.2 0.4 *4 197.3 0.5 *5 *1 The expanded uncertainty was based on the standard deviation of the mean. *2 The uncertainty of the median was based on the estimate from median(|xi-median|)/0.6745, where xi is each reported value. *3 The MMmedian was calculated according to the following: David L. Duewer, "A robust approach for the determination of CCQM key comparison reference values and uncertainties", Working document CCQM/04-15, BIPM, 2004, (www.bipm.info/cc/CCQM/Allowed/10/CCQM04-15.pdf). The uncertainty of the MMmedian was based on the estimate from median (|xi-median|)/0.6745, where xi is each reported value. *4 The square of reciprocal of reported uncertainty was used as a weight. *5 The reciprocal of reported uncertainty was used as a weight. The degree of equivalence (DoE) and its uncertainty between a participant result and the KCRV is calculated according to the following equations: Di = (xi – xR) Ui2 = (k2 ui2 + 22 uR2) where Di is the DoE between the participant's result xi and the KCRV, xR, and Ui is the expanded uncertainty (coverage factor k = 2) of Di calculated from both the combined standard uncertainty ui of xi and the standard uncertainty uR of xR . The calculation results are shown in Table 6 and Figure 2. The half of each bar in the Figure indicates Ui. 8 Table 6 Degree of equivalence for lead (CCQM-K88)* Participant Reported value Expanded / mass fraction uncertainty / mass (mg/kg) fraction (mg/kg) RV 197.2 INMETRO 179 VNIIM 194.2 NIM 195.8 NMIJ 196.7 KRISS 197.2 PTB 197.9 BAM 198.29 INTI 199 NIST 199.43 NRC 202.4 * Data from Table 4. 0.9 k=2 4 k=2 10 k=2 2.6 k=2 1.52 k=2 2 k=2 1.9 k=2 0.5 k=2 4 k=2 0.7 k=2 18.6 k=2 Di / mass fraction (mg/kg) Ui / mass fraction (mg/kg) Di / relative value (%) -18.2 -3.0 -1.4 -0.5 0.0 0.7 1.1 1.8 2.2 5.2 4.1 -9.2 10.0 -1.5 2.8 -0.7 1.8 -0.3 2.2 0.0 2.1 0.4 1.0 0.6 4.1 0.9 1.1 1.1 18.6 2.6 Ui / relative value (%) 2.1 5.1 1.4 0.9 1.1 1.1 0.5 2.1 0.6 9.4 Di / relative value (%) Degree of equivalence D i and expanded uncertainty U i . 10 Pb 5 0 -5 -10 INMETROVNIIM NIMNMIKJRISS PTBBAM INTINIST NRC Fig. 2 Degree of equivalence for Pb The half of each bar indicates Ui . 8 Demonstrated Core Capabilities The four tables of demonstrated core capabilities are attached as Annex B. At the IAWG meeting held November 1-2, 2011, it was decided to have a ‘how far does the light shine’ (HFDTLS) statement in the report as well as the tables of demonstrated core capabilities. With regard to HFDTLS, CMC claims based on determination of lead in this key comparison may be applied to other tin-based solders containing silver and copper provided that the concentration range of lead is 100 mg/kg to 2000 mg/kg and that those of silver and copper are less than 4 % and 6 % (mass fractions), respectively. The HFDTLS statement can be used for the participating institute to demonstrate ability to comply with the European WEEE and RoHS regulations, which was a major reason for organising this key comparison. 9 9 Acknowledgement The work of the key comparison was done with contributions from many scientists as well as the contact persons: Maren Koenig and Jochen Vogl (BAM), Lindomar Augusto dos Reis (INMETRO), Mabel Puelles, Nadia Hatamleh and Osvaldo Acosta (INTI), Jung Ki Suh, Hyung Sik Min and Youngran Lim (KRISS), Chao Jingbo, Feng Liuxing and Wei Chao (NIM), Savelas Rabb (NIST), Naoko Nonose (NMIJ), Brad Methven (NRC), Reinhard Jaehrling (PTB), Yu. A. Kustikov, S. B. Kozyreva and A. A. Korzh (VNIIM). 10 Annex A - Technical Protocol CCQM-K88 & P125 Key comparison and pilot study on determination of lead in lead-free solder containing silver and copper Call for participants and technical protocol (revised on July 14, 2010) Introduction Solder is one of ubiquitous materials in industry and elsewhere, and many people have recently been interested in lead-free solders from the viewpoint of the RoHS directive. Therefore, accurate measurements of lead in lead-free solders, especially containing silver and copper, are important. As the materials of CCQM comparisons in the field of metals and metal alloys, only low alloy steel (P25 and K33+P56) and copper alloy (P76 and K64) have been used. Since the main constituent of solders is usually tin, the recent pilot study P119 extended the field of comparisons to another important type of metals and metal alloys. The present key comparison K88 is a follow-up comparison of P119, and is carried out in parallel with the pilot study P125. Samples The comparison material is a lead-free solder (Sn 96.5 %, Ag 3 % and Cu 0.5 %) containing 100 mg/kg -600 mg/kg level of lead. The measurand to be determined is the mass fraction of lead. The material consists of short pieces (less than 0.1 g each) made by cutting long wires. Each participant will receive approximately 10 g of the lead-free solder. The homogeneity of the material was 0.8 % (rsd) according to the results of Pb based on ICP-OES determination using a sample size of about 0.2 g. Therefore, the use of more than 0.2 g sample for each measurement is strongly recommended. The sample after receiving should be kept at the laboratory temperature. No special treatment of the sample such as drying is required before use; however, it should be kept in a silica-gel desiccator before weighing. The CCQM-P125 sample is the same as the sample for CCQM-K88. Methods of Measurement Each participant can use any suitable method(s) of measurement. NMIs or officially designated institutes are welcome to participate in this comparison using primary methods of measurement. Four measurements for lead are to be carried out by each participant. The calibrations should be carried out by using standards with metrological traceability. Each participant’s capability of lead determination (approximately several hundred mg/kg) under the condition of the coexistence of tin and silver will be examined by the present comparison. The reference value will be probably a median of the submitted data from NMIs and officially designated institutes, though it will be decided after discussion in an IAWG meeting. Reporting The result should be reported as the mass fraction of lead to NMIJ (Akiharu Hioki), accompanied by a full uncertainty budget. Any participant that chooses to use multiple methods shall decide only one composite result (e.g., an average value from different methods). 11 Reporting the details of the procedure (including details of sample treatment/digestion), the calibration standard and the traceability link, and the instrument(s) used is required. A reporting form will be distributed to participants. Furthermore, please choose a suitable Core Capability table from the attached example forms and the filled-out table should be submitted together with the measurement result; if there is no suitable table, please make a suitable one depending on the measurement method. Time schedule Deadline of registration of participation: July 26, 2010 Dispatch of the samples: at the beginning of August, 2010 Deadline for receiving the report: December 31, 2010 Participants Participation is open to all interested NMIs or officially designated institutes that can perform the determination. An NMI or an officially designated institute is recommended to participate in the key comparison rather than in the pilot study as far as possible. An NMI or an officially designated institute may nominate other institutes or laboratories to participate in the pilot study. Please inform NMIJ (Akiharu Hioki) of the contact person, the shipping address, and so on using the attached registration form. Even if you do not wish to participate, please inform NMIJ of it. We would like to ask NMIs or officially designated institutes to coordinate participation within their economies including inviting participants in the pilot study, shipping samples, and receiving the reports. The coordinating laboratories might invite some expert laboratories directly to participate in the pilot study. Coordinating laboratories Dr. Akiharu HIOKI National Metrology Institute of Japan (NMIJ), AIST Tsukuba Central 3-9, 1-1-1, Umezono, Tsukuba, Ibaraki, 305-8563, Japan Tel: +81-29-861-9341 or +81-29-861-6881 Fax: +81-29-861-6890 E-mail: aki-hioki@aist.go.jp Dr. MA Liandi National Institute of Metrology (NIM), No. 18, Bei San Huan Dong Lu, Chaoyang District, Beijing, 100013, P. R. China Tel: +86-10-6422-3987 Fax: +86-10-6422-3987 E-mail: mald@nim.ac.cn Dr. Kyung-Haeng CHO Korea Research Institute of Standards and Science (KRISS), 1 Doryong-Dong, Youseong-Gu, Daejeon, 305-340, Rep. of Korea Tel: +82-42-868-5363 Fax: +82-42-868-5802 E-mail: chokh@kriss.re.kr 12 Annex B - Tables of Demonstrated Core Capabilities Demonstrated Inorganic Core Capabilities (1) CCQM-K88, Lead in Lead-Free Solder Analyte: Pb Methodology: ID-ICP-MS Participating Institutes: NMIJ, NIM, KRISS, PTB Instructions: List institutes demonstrating capabilities Capabilities/Challenges Not Tested Tested Contamination control and correction All techniques and procedures employed to reduce potential contamination of samples as well as blank correction procedures. The level of difficulty is greatest for analytes that are environmentally All ubiquitous and also present at very low concentrations in the sample. Specific Challenges Encountered Lead remains a common contaminant at trace levels demanding use of clean reagents, vessels and hyandling procedures to not only minimize the blank, but generate a consistent one. Digestion/dissolution of organic matrices All techniques and procedures used to bring a sample that is primarily organic in nature into All solution suitable for liquid sample introduction to the ICP. Digestion/dissolution of inorganic matrices All techniques and procedures used to bring a sample that is primarily inorganic in nature into solution suitable for liquid sample introduction to the ICP. Volatile element containment All techniques and procedures used to prevent the loss of potentially volatile analyte elements during All sample treatment and storage. Pre-concentration Techniques and procedures used to increase the concentration of the analyte introduced to the ICP. Includes evaporation, ion-exchange, extraction, All precipitation procedures, but not vapor generation procedures. No organic components within this sample Co-existence of tin and silver should be considered in order to determine the All optimal digestion approach; precipitation of tin oxides and silver halides may be problematic The measurand is not volatile with respect to the sample processing conditions and no losses are expected, especially when digestion is undertaken in high pressure closed vessels. No preconcentration or matrix separation techniques were needed as the amount content of the measurand was sufficient to allow for simple dilution of the digested matrix. Vapor generation Techniques such as hydride generation and cold All vapor generation used to remove the analyte from the sample as a gas for introduction into the ICP. Matrix separation Techniques and procedures used to isolate the analyte(s) from the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Techniques and procedures used to isolate the analyte(s) from All the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Direct sample introduction techniques were used. No preconcentration or matrix separation techniques were needed as the amount content of the measurand was sufficient to allow for simple dilution of the digested matrix. Spike equilibration with sample The mixing and equilibration of the enriched isotopic spike with the sample. Signal detection The detection and recording of the analyte isotope signals. The degree of difficulty increases for analytes present at low concentrations, of low All All 13 ID-MS requires spike equilibration to ensure identical behaviour of the endogenous and added forms of lead from the start of any sample processing. The amount content of the measurand was sufficient to generate good signal-tonoise characteristics Capabilities/Challenges isotopic abundance, or that are poorly ionized. Memory effect Any techniques used to avoid, remove or reduce the carry-over of analyte between consecutively measured standards and/or samples. Not Tested Correction or removal of isobaric/polyatomic interferences Any techniques used to remove, reduce, or mathematically correct for interferences caused by mass overlap of analyte isotopes with isobaric or polyatomic species. Includes collision cell techniques, high resolution mass spectrometry, or chemical separations. The relative concentrations and sensitivities of the analyte isotopes and the interfering species will affect the degree of difficulty. Detector deadtime correction Measurement of, and correction for, ion detector deadtime. Importance increases in situations where high ion count rates are encountered. Mass bias/fractionation control and correction Techniques used to determine, monitor, and correct for mass bias/fractionation. Spike calibration Techniques used to determine the analyte concentration in the enriched isotopic spike solution. Tested All All All All All Specific Challenges Encountered Lead does not suffer significant memory effects with standard sample introduction systems but care should be exercised when alternating between spiked solutions containing enriched isotopes and the unspiked sample Alhough the 200 Da region of the mass spectrum is relatively free of background counts and interferences from molecular ions, these need to be carefully checked, along with elemental isobaric interferences and corrections made when required Standard deadtime correction equations were utilized to correct response. Determination of the isotope composition of Pb in the sample is required.Usually isotopic ratio and matrix component of spike sample and those of isotopic standard solution (e.g., NIST SRM 982) are different. Therefore, careful handling of these solutions is necessary; for example, insertion of washing stage between the solutions to reduce memory effect. Careful assessment of the amount content of the enriched spike is required, using a reverse ID-MS approach and a traceable calibration standard of known iostopic composition 14 Demonstrated Inorganic Core Capabilities (2) CCQM-K88, Lead in Lead-Free Solder Analyte: Pb Methodology: ID-TIMS Participating Institutes: BAM Instructions: List institutes demonstrating capabilities Capabilities/Challenges Not Tested Tested Contamination control and correction All techniques and procedures employed to reduce potential contamination of samples as well as blank correction procedures. The level of difficulty is greatest for analytes that are environmentally ubiquitous and also present at very low concentrations in the sample. BAM Specific Challenges Encountered Lead remains a common contaminant at trace levels demanding use of clean reagents, vessels and hyandling procedures to not only minimize the blank, but generate a consistent one. Digestion/dissolution of organic matrices All techniques and procedures used to bring a sample that is primarily organic in nature into solution suitable for subsequent analyte-matrix separation. BAM No organic components within this sample Digestion/dissolution of inorganic matrices All techniques and procedures used to bring a sample that is primarily inorganic in nature into solution suitable for subsequent analyte-matrix separation. BAM Co-existence of tin and silver should be considered in order to determine the optimal digestion approach; precipitation of tin oxides and silver halides may be problematic Spike equilibration with sample The mixing and equilibration of the enriched isotopic spike with the sample. Volatile element containment All techniques and procedures used to prevent the loss of potentially volatile analyte elements during sample treatment and storage. Matrix separation Techniques and procedures used to remove the sample matrix and isolate the analyte element for subsequent loading on the filament. Includes evaporation, ion-exchange, extraction, precipitation procedures or others. Test of recovery and potential mass fractionation. Conversion to chemical form for TIMS Techniques and procedures to convert the analyte into a chemical form required for TIMS measurements, e.g. conversion of sulfate into As2S3 for sulfur measurements. Filament preparation chemistry and loading Techniques and procedures used to load the analyte onto filaments and prepare them for measurement. Signal detection The detection and recording of the analyte isotope signals. The degree of difficulty increases for analytes present at low concentrations, of low isotopic abundance, or that are poorly ionized. BAM BAM BAM BAM BAM BAM ID-MS requires spike equilibration to ensure identical behaviour of the endogenous and added forms of lead from the start of any sample processing. The measurand is not volatile with respect to the sample processing conditions and no losses are expected. TIMS requires careful separation of matrix components without perturbation of the isotopic composition of the measurand Standard procedure for Pb measurements has been used, this point has been tested during procedure development and validation Standard procedure for Pb measurements has been used, this point has been tested during procedure development and validation Standard procedure for Pb measurements has been used, this point has been tested during procedure development and validation Ion signal generation Procedures for warm up, filament heating and measurement procedures BAM 15 Standard procedure for Pb measurements has been used, this point has been tested during procedure development and Capabilities/Challenges Not Tested Correction or removal of isobaric/polyatomic interferences Any techniques used to remove, reduce, or mathematically correct for interferences caused by mass overlap of analyte isotopes with isobaric or polyatomic species. Includes warm up and filament heating procedures, high resolution mass spectrometry, or mathematical corrections. The relative concentrations and sensitivities of the analyte isotopes and the interfering species will affect the degree of difficulty. Detector deadtime correction Measurement of and correction for the deadtime of ion counting detectors if applicable. BAM Correction of mass fractionation Techniques used to determine, monitor, and correct for instrumental and procedural mass fractionation. Spike calibration Techniques used to determine the analyte concentration in the enriched isotopic spike solution. Tested Specific Challenges Encountered validation Checked for interferences, but no interferences oc cur BAM BAM BAM Not applicable as Faraday detectors have been used Determination of the isotope composition of Pb in the sample is required. Double IDMS applied 16 Demonstrated Inorganic Core Capabilities (3) CCQM-K88, Lead in Lead-Free Solder Analyte: Pb Methodology: ICP-OES Participating Institutes: INMETRO, VNIIM, INTI, NIST Instructions: List institutes demonstrating capabilities Capabilities/Challenges Not Tested Tested Contamination control and correction All techniques and procedures employed to reduce potential contamination of samples as well as blank correction procedures. The level of difficulty is greatest for analytes that are environmentally All ubiquitous and also present at very low concentrations in the sample. Specific Challenges Encountered Lead remains a common contaminant at trace levels demanding use of clean reagents, vessels and hyandling procedures to not only minimize the blank, but generate a consistent one. Digestion/dissolution of organic matrices All techniques and procedures used to bring a sample that is primarily organic in nature into solution suitable for liquid sample introduction to All the ICP. No organic components within this sample Digestion/dissolution of inorganic matrices All techniques and procedures used to bring a sample that is primarily inorganic in nature into solution suitable for liquid sample introduction to the ICP. Volatile element containment All techniques and procedures used to prevent the loss of potentially volatile analyte elements during sample treatment and storage. Pre-concentration Techniques and procedures used to increase the concentration of the analyte introduced to the ICP. Includes evaporation, ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Vapor generation Techniques such as hydride generation and cold vapor generation used to remove the analyte from the sample as a gas for introduction into the ICP. Matrix separation Techniques and procedures used to isolate the analyte(s) from the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Techniques and procedures used to isolate the analyte(s) from the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Calibration of analyte concentration The preparation of calibration standards and the strategy for instrument calibration. Includes external calibration and standard additions procedures. Signal detection The detection and recording of the analyte signals. The degree of difficulty increases for analytes present at low concentrations, or that are have weak emission lines.. All All All All All All All 17 Co-existence of tin and silver should be considered in order to determine the optimal digestion approach; precipitation of tin oxides and silver halides may be problematic and result in loss of measurand The measurand is not volatile with respect to the sample processing conditions and no losses are expected, especially when digestion is undertaken in high pressure closed vessels. No preconcentration or matrix separation techniques were needed as the amount content of the measurand was sufficient to allow for simple dilution of the digested matrix. Direct sample introduction techniques were used. No preconcentration or matrix separation techniques were needed as the amount content of the measurand was sufficient to allow for simple dilution of the digested matrix. Calibration standards prepared from traceable reference materials, requires accurate (gravimetric) dilution. Good signal-to-noise ratio must be achieved. Lead is not a particularly sensitive element by atomic emission. Capabilities/Challenges Not Tested Memory effect Any techniques used to avoid, remove or reduce the carry-over of analyte between consecutively measured standards and/or samples. Complex spectral backgrounds Any techniques used to remove, reduce, or mathematically correct for interferences caused by the overlap of analyte emission lines with atomic, ionic, or molecular emission from matrix components. The relative concentrations and sensitivities of the analyte and the interfering species will affect the degree of difficulty. Samples containing high concentration matrix components with large numbers of emission lines or molecular bands may increase the measurement challenge. Correction or removal of matrix-induced signal suppression or enhancement Chemical or instrumental procedures used to avoid or correct for matrix-induced signal suppression or enhancement. High concentrations of acids, dissolved solids, or easily ionized elements will increase the degree of difficulty. Tested All All All Specific Challenges Encountered Lead does not suffer significant memory effects with standard sample introduction systems but care should be exercised when alternating between samples, calibrants and blanks The Pb(II) 220.353 nm line is realtively free of major interferences from other lines but care must be exercised in establishing baseline levels for intensity evaluations. The relatively low concentration of Pb requires low sample dilution factors and thus greater susceptibility to matrix interference. 18 Demonstrated Inorganic Core Capabilities (4) CCQM-K88, Lead in Lead-Free Solder Analyte: Pb Methodology: GD-MS Participating Institutes: NRC Instructions: List institutes demonstrating capabilities Capabilities/Challenges Not Tested Tested Contamination control and correction All techniques and procedures employed to reduce potential contamination of samples as well as blank correction procedures. The level of difficulty is greatest for analytes that are environmentally ubiquitous and also present at very low concentrations in the sample. NRC Volatile element containment All techniques and procedures used to prevent the loss of potentially volatile analyte elements during sample treatment and storage. NRC Sample preparation Techniques and procedures used to render the test sample into a form compatible with GD pin cell geometry, including machining, cutting, pressing , forming (e.g., Ga) or otherwise mounting (e.g., pressing onto In) to achieve required geometry. NRC Matrix separation Techniques and procedures used to isolate the analyte(s) from the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Techniques NRC and procedures used to isolate the analyte(s) from the sample matrix to avoid or reduce interferences caused by the matrix. Includes ion-exchange, extraction, precipitation procedures, but not vapor generation procedures. Calibration of analyte concentration The preparation of calibration standards and the strategy for instrument calibration. Includes external calibration and standard additions procedures. NRC Signal detection The detection and recording of the analyte signals. The degree of difficulty increases for analytes present at low concentrations, or that are have weak emission lines.. NRC Memory effect Any techniques used to avoid, remove or reduce the carry-over of analyte between consecutively measured standards and/or samples. NRC Complex spectral backgrounds Any techniques used to remove, reduce, or mathematically correct for interferences caused by the overlap of analyte emission lines with atomic, ionic, or molecular emission from matrix components. The relative concentrations and NRC sensitivities of the analyte and the interfering species will affect the degree of difficulty. Samples containing high concentration matrix components with large numbers of emission lines or molecular bands may increase the measurement challenge. Correction or removal of matrix-induced signal suppression or enhancement Chemical or instrumental procedures used to avoid or correct for matrix-induced signal suppression or NRC enhancement. High concentrations of acids, dissolved solids, or easily ionized elements will increase the degree of difficulty. Specific Challenges Encountered Chemical surface etching of sample under clean conditions followed by sputter cleaning of sample surface in the GD. The measurement technique utilizes the solid sample for testing and losses are not possible. Pin geometry identical to matrix matched standard used for calibration Solid sampling is undertaken with no dissolution or matrix separation. Calibration in this exercise performed with matrix matched “standard” NMIJ CRM 8203-a Ratioing technique between ion and faraday detectors with cross-calibration using Ar ions Cells pre-sputtered for each sample prior to data collection “Medium” resolution (4000) MS measurements performed with sector field instrument to separate molecular ion interferences Ratioing technique with calibration against matrix matched standard for this exercise (NMIJ CRM 8203-a) 19 20Ver+/- |